C | Si | Mn | P | S | Cr | Mo | V |
0.34-0.38 | ≤0.50 | ≤0.50 | ≤0.015 | ≤0.001 | 4.80-5.20 | 1.80-2.20 | 0.40-0.60 |
热膨胀系数 【10-6m/(m x K)】 | 20-100°C | 20-200°C | 20-300°C | 20-400°C | 20-500°C | 20-600°C | 20-700°C |
11.9 | 12.4 | 12.6 | 12.7 | 13.0 | 13.1 | 13.4 | |
热传导性 【W/(m x K)】 | 20°C | 350°C | 700°C | | | | |
29.7 | 31.0 | 33.2 | | | | |
段造 | 软性退火 | 淬 硬 | 回 火 |
1050-850°C | 820-840°C | 1020-1050°C | 520-700°C |
出厂状态 | 运用状态 | 钢材组织 |
EFS退火精细化退火至硬度≤220HB | 30-56 HRC | |