型号 | VK-RYK1 | VK-RYK1B | VK-RYK2 | VK-RYK3 |
晶相 | 3Y四方相 | 3Y四方相 | 5Y四方相 | 8Y立方相 |
ZrO2% (+ HfO2) | 94.7±0.3 | 94.7±0.3 | 91.5±0.3 | 86.5±0.3 |
Y2O3(wt%) | 5.3±0.3 | 5.3±0.3 | 8.5±0.3 | 13.5±0.3 |
Al2O3% ≤ | 0.01 | 0.01 | 0.01 | 0.01 |
SiO2%≤ | 0.01 | 0.01 | 0.01 | 0.01 |
Fe2O3%≤ | 0.01 | 0.01 | 0.01 | 0.01 |
CaO%≤ | 0.005 | 0.005 | 0.006 | 0.005 |
MgO%≤ | 0.005 | 0.005 | 0.005 | 0.005 |
TiO2%≤ | 0.002 | 0.002 | 0.002 | 0.002 |
Na2O%≤ | 0.005 | 0.004 | 0.005 | 0.005 |
Cl- %≤ | 0.1 | 0.1 | 0.1 | 0.1 |
灼减%≤ | 0.8 | 0.8 | 0.8 | 0.8 |
比表面积(m2/g) | 13±2 | 13±2 | 13±2 | 13±2 |
黏合剂(wt%) | - | 2 | - | - |
平均粒径 um | 50±5um | 50±5um | 50±5um | 50±5um |